光泽低，良好的流动性，耐热性高，汽车内部零件

 

Lustran® Elite HH ABS 1827

丙烯腈丁二烯苯乙烯

 

INEOS ABS (USA)

 

Technical Data

 

产品说明

 

Lustran® Elite HH ABS 1827 resin is an injection molding grade of ABS (Acrylonitrile Butadiene Styrene) for high-heat applications in the automotive market. With a Vicat softening temperature of 233°F (112°C), Elite HH 1827 provides high heat resistance, low gloss, toughness, and easy flow for processing molded-in color parts. The resin is available in natural and black colors only. Its consistent, clean, natural color makes it ideally suitable for use with color concentrates. Color concentrates for automotive color matches are available from several concentrate suppliers.

 

Lustran Elite HH ABS 1827 resin offers the right balance of properties for a variety of above-the-belt-line automotive applications. It is used for parts in the sun-loaded area where low-gloss, molded-in color is desired. Typical applications include A & B pillars, door panels, sail panels, consoles and console trim, cowl vents, and lamp housings. As with any product, use of Lustran Elite HH ABS 1827 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

UL 黄卡 2 •  E44741-235657

搜索 UL 黄卡 •  INEOS ABS (USA)

•  Lustran® Elite

供货地区 • 北美洲

特性 • 光泽，低 • 良好的着色性 • 韧性良好

• 良好的流动性 • 耐热性，高

用途 • 汽车领域的应用 • 汽车内部零件

机构评级 • EC 1907/2006 (REACH)

外观 • 黑色 • 自然色

形式 • 粒子

加工方法 • 注射成型

 

物理性能 额定值单位制 测试方法

比重 1.05g/cm³ ASTM D792

特定体积 0.950cm³/g ASTM D792

熔流率（熔体流动速率） ASTM D1238

220°C/10.0 kg 13g/10 min

230°C/3.8 kg 4.0g/10 min

收缩率 - 流动 0.40 到 0.70% ASTM D955

机械性能 额定值单位制 测试方法

抗张强度

屈服 39.3MPa ASTM D638

屈服 42.0MPa ISO 527-2

伸长率 (断裂) 50% ASTM D638

弯曲模量

-- 2340MPa ASTM D790

-- 2350MPa ISO 178

弯曲强度 (屈服) 69.6MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度

23°C, 3.18 mm 180J/m ASTM D256

23°C, 6.35 mm 130J/m ASTM D256

23°C, 12.7 mm 120J/m ASTM D256

-40°C 4 7.7kJ/m² ISO 180/1A

23°C 4 17kJ/m² ISO 180/1A

 

 

 

Lustran® Elite HH ABS 1827

丙烯腈丁二烯苯乙烯

INEOS ABS (USA)

热性能 额定值单位制 测试方法

载荷下热变形温度 ASTM D648

0.45 MPa, 未退火, 3.18 mm 95.0°C

1.8 MPa, 未退火, 3.18 mm 82.8°C

1.8 MPa, 未退火, 6.35 mm 92.8°C

1.8 MPa, 未退火, 12.7 mm 96.1°C

维卡软化温度

-- 112°C ASTM D1525 5

-- 101°C ISO 306/B50

线形热膨胀系数 - 流动 (-30 到 30°C) 8.3E-5cm/cm/°C ASTM D696

RTI Elec (1.50 mm) 60.0°C UL 746

RTI Imp (1.50 mm) 60.0°C UL 746

RTI (1.50 mm) 60.0°C UL 746

可燃性 额定值单位制 测试方法

燃烧速率 6 51mm/min SAE J1685

UL 阻燃等级 UL 94

1.50 mm HB

3.20 mm HB

注射 额定值单位制

干燥温度 82.2 到 87.8°C

干燥时间 2.0hr

建议的最大水分含量 < 0.10%

建议的最大回制料比例 20%

料筒后部温度 238 到 254°C

料筒中部温度 243 到 260°C

料筒前部温度 249 到 266°C

射嘴温度 249 到 266°C

加工（熔体）温度 249 到 271°C

模具温度 48.9 到 71.1°C

注塑压力 89.6 到 138MPa

注射速度 快速

背压 0.172 到 0.689MPa

锁模力 2.8 到 5.5kN/cm²

垫层 < 6.35mm

螺杆长径比 20.0:1.0

螺杆压缩比 2.5:1.0

注射说明

Hold Pressure: 50 to 75% of Injection Pressure

Screw Speed: Moderate

Drying at 4 hours at 160°-170°F is also adequate.

 

 

 

 

 